Avoid Surface Defects on Interior Slabs

Building owners expect steel troweled floors to be smooth, hard, attractive and free of surface defects. As you know, easier said than done! With environmental conditions changing daily and perhaps hourly, flatwork finishers must be able to read the concrete and respond appropriately to avoid surface defects.

Avoid premature finishing

Wait to start power floating until the bleed water sheen has disappeared and the concrete has stiffened sufficiently to support a finisher with no more than a ¼ inch footprint indentation. Failure to do so results in bleed water being finished into the top surface or the surface being prematurely sealed.

Finishing bleed water into the surface. Bleed water is extra mix water that rises and collects on the surface of the concrete when the bleed rate of the concrete exceeds the surface evaporation rate. Finishing the bleed water into the top surface increases the water to cementitious material (w/cm) ratio on the top surface, which decreases the surface strength of the concrete and makes the surface more prone to premature wear, dusting and crazing. Other causes that produce the same effect include too much mix water, high w/cm ratios, overworking overly wet mixes, premature floating, improper or inadequate troweling, and inadequate curing.

If surfaces have stiffened or hardened sufficiently for power floating but the bleed water has not evaporated, drag a rubber hose or compressor hose across the surface and remove the water. Also, do not add and finish water into the surface to facilitate finishing because the surface has dried due to rapid evaporation. Finishing added water into the top surface has the same detrimental effects as finishing bleed water into the surface, as seen in Image 1.

Dusting is the development of a fine powdery material consisting of water, cement and fine particles that easily rubs off the top surface of interior floors. Mixing bleed or added water into the surface dilutes the mortar phase of the concrete and creates a thin, weak layer of mortar called laitance along the top surface. Other causes of dusting are overusing vibrating screeds, finishing overly wet mixes, insufficient cement, excessive clay or dirt in the aggregates, using dry cement to soak up bleed water, carbonation of the surface related to unvented heaters, freezing of the surface and inadequate curing.

Crazing is the chicken-wire-like pattern of fine cracks that are barely visible and sometimes only visible when the concrete is drying after the surface has been wet. Since crack depths are very shallow, this form of surface cracking is primarily an aesthetic concern. Crazing seldom creates structural or serviceability issues, even for floors exposed to heavy forklift traffic. Crazing is caused by minor surface shrinkage related to rapid surface drying and wetting-and-drying cycles. Many of the causes listed above for dusting also contribute to crazing, especially overworking overly wet mixes and finishing bleed or added water into the top surface.

Trapping bleed water and air. When mix water migrates upward because the cement and aggregate particles are settling, the surface must be “open” so as not to trap the rising bleed water and air directly beneath the top surface. Trapping bleed water and air creates a thin, weak zone directly beneath the surface and results in surface blisters or delaminations. Blisters and delaminations typically form during the onset of troweling. Blisters range in diameter from 14 to 4 inches and typically about 18-inch deep, whereas surface areas for delaminations are larger and can range from a few square inches up to several square feet or more and depths vary from about 18 to 38 inch.

Premature sealing often occurs when the top surface stiffens due to surface drying or the top surface is setting faster than the underlying concrete. Top down setting often occurs when the ground temperatures are cool but the ambient conditions are warm and sunny. When this happens, flatwork finishers mistakenly believe the slab is ready to be power floated or troweled. However, the bleed water and air are still rising. If the finishers seal the surface prematurely, then rising water and air become trapped beneath the surface.

To offset early surface drying and top down setting, plan ahead and be prepared for these situations. Use water foggers and evaporation retarders to avoid early surface drying. Offset top-down setting by warming the base material or accelerating concrete setting with chemical admixtures. Be aware of these challenging conditions and do not seal the surface during bull floating or restraightening and wait until bleeding has ceased before power floating.

Do not power trowel air-entrained concrete. Many finishers have learned the hard way that power troweling air-entrained, normal-weight concrete is extremely risky. Purposely entrained air delays bleeding and increases the possibility of prematurely sealing surfaces. ACI 302.1R-04 Guide for Concrete Floor and Slab Construction recommends not specifying or using air-entraining agents for concrete to be given a smooth, dense, hard-troweled finish because blistering or delaminations may occur. ACI 302 also states that blisters and delaminations can occur any time when the total air content (entrained and entrapped air bubbles) exceeds 3 percent. Always review and check the specifications, proposed mix designs and delivery tickets for air-entraining admixtures so you do not unknowingly power trowel air-entrained, normal-weight concrete. Some finishers routinely perform air tests on the freshly mixed concrete before discharging to ensure the total air content does not exceed 3 percent.

Surface densification

Power troweling should create dense, smooth, hard surfaces. By progressively increasing the angle of the steel trowel blades against the top surface of a slab, the surface mortar is increasingly densified by expelling free water and air. Proper troweling produces a densified surface layer (DSL) with typical thicknesses varying between about 1 to 4 mm (364 to 532 inches). As shown in Image 2, the DSL is identified by its dark color as compared to the underlying concrete. The dark color is also visible on the top surface of the slab and commonly referred to as “burnishing” or a “burnished” surface.

In order to produce a burnished surface, repeatedly trowel the slab while incrementally increasing the trowel blade angle so as to continually increase the blade pressure on the surface. If blade angles are increased too fast relative to the stiffness of the surface, “blade chatter” can occur as shown in Image 3. Floors subject only to light troweling or floors with DSL thicknesses less than 1 mm (364 in.) may be prone to premature surface wear, especially if exposed to a high frequency of small, hard-wheeled forklift traffic.

Inadequate protection and curing

To avoid surface defects associated with drying of the surface including crusting, crazing, dusting and reduced surface strength, favorable moisture and temperature conditions must be maintained throughout the finishing process. Plastic-shrinkage cracking is typically not a problem for interior slabs because power floating and troweling keeps closing surface tears and cracks caused by surface drying. However, other surface drying defects can occur when surfaces are not protected from early drying and final curing is delayed.

Crusting occurs when the top surface becomes stiff due to excessive surface drying but the underlying concrete is still plastic. Slabs that crust are difficult to finish and typically result in a wavy, cracked surface and are prone to premature surface wear and delaminations.

To offset early surface drying, use water foggers and evaporation retarders. Do not use evaporation retarders as a finishing aid. That is, do not apply evaporation retarders to facilitate finishing because the surface has dried and become too stiff to finish. After mixing, evaporation retarders are typically 90 percent water so it is not acceptable to finish or mix an evaporation retarder into the top surface of the concrete. Start final curing immediately after troweling or saw cutting.

Premature finishing can lead to costly surface defects while waiting too long to start power floating and troweling may result in unacceptable floor flatness and surface finishes. The true challenge in finishing interior concrete floors is finding the window of finishability regardless of the changing and adverse placing conditions.

References:

  • ACI 302.1R-04 Guide for Concrete Floor and Slab Construction, American Concrete Institute, Farmington Hills, Mich., www.concrete.org.

• Craftsman Workbook CP-10 (05) ACI Certification Program for Concrete Flatwork Technician and Finisher, American Concrete Institute, Farmington Hills, Mich., www.concrete.org.

 

Kim Basham is president of KB Engineering LLC (www.kbengllc.com), which provides engineering and scientific services to the concrete industry. Basham also teaches seminars and workshops dealing with all aspects of concrete technology, construction and troubleshooting. David Rothstein, Ph.D, P.G., FACI is principal of DRP Consulting, Inc. (www.drpcinc.com), a firm located in Boulder, Colo., that specializes in petrographic and materials investigations.