Altering sealer mix design

Sealcoating professionals often ask how to adjust mix design for weather-related conditions, for sand/aggregate loadings, or simply for the amount of water in the mix.

Contractors can make these adjustments, and should make them in consultation with their sealer producer. But before tinkering with recommended mix designs it is imperative to understand some fundamentals that relate to film formation and the factors which influence the proper set and final cure of sealer films.

Let's start with the basics - sealer composition, film formation, and the conditions for proper film formation - before finally discussing the adjustment of mix designs.

Some sealcoating basics
Most sealcoatings are intimate dispersions of refined coal tar or asphalt cement, clay, emulsifiers and specialty chemicals in water. Being water-based, sealcoatings are safe to handle and store. Over the decades it has been established that sealcoatings provide years of protection to asphalt surfaces when applied properly and allowed to cure under the right ambient conditions.

The major components of a sealer are:

  • Refined coal tar or asphalt is the binder or the glue that holds the inorganic fillers (clay, sand/aggregate, etc.) tightly bound in the sealer film after full cure. Both asphalt and coal tar are thermoplastic materials, meaning that they soften and melt at higher temperatures (about 100°F to 180°F, higher for asphalt) and become hard at cooler temperatures (below 60°F).
  • Binder is the backbone of sealcoating. It is the component that protects the asphalt in the pavement. In the wet (uncured) state, sealer contains a fine dispersion of binder particles in the range of 2 to 5 microns (human hair is approximately 25 microns), either in spherical or elongated cigar shapes. Upon full cure the binder forms a continuous film, enveloping the filler particles (1 to 2 microns) thus holding them tightly in the cured film.
  • Clay, fillers, and aggregates impart toughness and dimensional stability to sealcoating film and counteract the tackiness of binder at elevated surface temperatures.
  • Specialty chemicals, such as surfactants and emulsifiers, keep the binder and filler particles properly suspended and dispersed in the wet state, providing a stable system.
  • Water is the fluid medium in which the above components are dispersed.

Mix designs
Sealcoatings are usually supplied in a concentrated form, which have to be mixed with water, sand/aggregate, and additives (optional), prior to application.

  • Water gives fluidity to the sealer, and also satisfies the water demand of sand. All fillers absorb water (called their "water demand") which has to be satisfied by water in the mix. Fillers also absorb the binder which is called the binder demand. Water also wets out the pavement for proper flow, leveling, and adhesion of the sealer to the pavement.
  • Sand /aggregate imparts slip resistance and traction, provides uniform textured, non-streaky appearance with reduced sun glare, improves wearability, and hides minor surface defects.
  • Additives are added to enhance the performance, speed up drying or sand suspension, or all of the above. There are many additives that are recommended to perform specific functions in sealer mix designs.

Mix designs are simply the guideline for the proportions in which these components are to be mixed according to the usage requirements of the pavement. For example, low traffic flow may require low water of dilution, low sand loading, and a one coat application. Conversely, medium traffic volume may require more water, more sand, and the use of an additive. Mix designs are also adjusted to accommodate weather conditions and/or varying amounts of fillers, additives, etc.

The cure & film formation mechanism
Water is the major component of sealcoatings. The sealer supplied as a concentrate typically contains 60% water by volume. After adding 30% water to 100 gallons of the concentrated sealer, the water proportion increases to nearly 70%, by volume.

Sealcoatings, being water-based, attain full cure through the loss of all the water from the wet film. As the water leaves, the volume of the wet film shrinks in proportion to the amount of water (by volume) in the mix. For example, if the mix design has 70% water by volume the wet film will shrink by 70%, or down to 30% of the original volume.

As the water evaporates, it creates a steady turbulence in the sealer film, which forces the suspended particles (binder, filler) into a closer proximity. The film becomes progressively denser, thus forcing the binder particles to touch each other and fuse into a continuous film, encapsulating the filler particles in the process. Simultaneously, the binder bonds to the pavement.

Properly cured sealcoatings form a continuous film, free of voids or imperfections, which stop water, chemicals, salts, etc. from penetrating and damaging the asphalt pavement underneath. Understandably, any deficiency in the curing process will not allow the binder to fuse properly and leave voids in the film, thus resulting in inferior performance or failure.

A closer look at the sealer film
The wet sealcoating film is not one solid film but a composite of several layers of very thin films (imagine a sheet of plywood). Like most water-based coatings, sealcoating dries in successive layers from top to bottom. As each layer dries, it shrinks in volume and becomes tight and relatively impervious to water vapor, therefore, impeding the evaporation of water from the bottom layers.

The first 80% to 85% of the film dries relatively fast, but the release of the last 10% to 15% of water becomes difficult and requires the right set of ambient and pavement conditions. It's a fact that the release of water from the bottom layers of most water-based coatings becomes progressively difficult as the film cures. For optimum performance, all water must leave the film; 80% to 90% is not good enough. The uncured 10% to 15% of the coating will be torn or dislodged if traffic is allowed on it too soon. The percentages are mentioned here only to explain the phenomenon. They will, of course, vary with material and mix designs, e.g. mix designs with fillers and/or aggregates will dry faster than sealcoatings without them.

The cure conditions
Pavement and ambient temperature, relative humidity, and wind velocity have a very profound effect on the rate of water release from wet sealer film and the final cure.

Temperature, both ambient and pavement, influences both aspects in the proper film formation and final cure - release of water and fusion of binder particles.

Cold Temperatures: The minimum recommended application temperature for a sealer is 50°F and rising. The fusion of the binder particles to form a continuous film is greatly enhanced at higher temperatures. Conversely, it is significantly reduced at temperatures below 50°F.

When sealcoating is applied below 50°F, tar (or asphalt) particles do not soften and form a continuous film, thus leaving clay and filler particles uncoated. The color of the sealer cured under such conditions usually turns out grey and blotchy in appearance and never returns to its normal slate black appearance, even at higher pavement temperatures, because the temperature of the pavement normally does not reach high enough to re-melt the binder particles and force them to flow and form a continuous film.

Even if the pavement temperature reaches high enough it still will not assure proper fusion. The binder particles will melt but will not have the capability to flow and envelope the clay and filler particles already set in a rigid matrix.

Needless to say sealcoating cured under cold weather conditions lacks the film integrity and the expected performance properties.

Mix design alteration suggestion:
Consider using an additive (1% to 2% on sealer volume) that will help the sealer dry faster. Such additives contain fast-evaporating solvents which combine with water in the sealer, accelerating the evaporation rate, at low temperatures. Most rubberizing (performance-boosting) type additives also speed up the water evaporation. Such additives form a polymer network within the sealer film, which forces the water out of the film at a uniform rate.

Another possibility is to reduce the water of dilution as much as possible. Use the lower limit recommended by the sealer producer.

Hot Temperatures: Sealcoating applications under hot temperatures can be equally problematic. Sealcoatings should not be applied under the summer sun (90°F ambient) without first cooling the surface. If applied to a hot pavement that is too hot the sealcoating film almost gets "baked" as soon as it hits the pavement, resulting in a film full of pinholes.

The sudden loss of water immobilizes binder particles in the sealer and prevents them from fusing into each other and forming a continuous film. Devoid of the proper fusion process, binder particles do not effectively envelop the clay and filler particles in the sealer film.

As a result, binder stays as discrete particles not hardened by clay and filler particles. The sealer film, under such cure condition, may not reach the hardness and continue to stay sticky and soft. And that could lead to lead to a "tracking" problem, where the sealer may be tracked into the buildings and onto the carpet or tiles.

Mix design alteration suggestions:
Cool the pavement with a fine mist of water ("fogging"). Avoid puddling, otherwise sealer may just slide right off during application.

Not as effective as fogging but an acceptable and generally used approach is to add more water in the mix (3% to 5%), to increase fluidity.

Relative Humidity: Relative humidity (often referred to simply as humidity) is another major factor that greatly influences the film formation and final cure of the sealer. Relative humidity is the ratio of the actual moisture content of the air, at a specified temperature, to its total capacity. For example, 50% relative humidity means that only half of the air's total capacity is used and it is capable of absorbing another 50% of moisture or vapor from surroundings.

Conversely, at 90% relative humidity the air has very little capacity left (only 10%) to absorb additional moisture, thus drastically slowing down the release of water (cure) from the sealcoating film. The sealer film will release only the amount of water that can be accommodated by the atmosphere.

The atmosphere and the surrounding environment can be thought of as a sheet of paper towel: When dry it will soak up the spill, but it will not soak up the spill if the towel is too wet.

At 100% relative humidity the sealer film may take several hours, if not days, to cure.

The slow cure is further aggravated by low temperatures. For example, the rate of water evaporation is nearly halved for a 10-degree drop in temperature, at a given relative humidity.

Mix design alteration suggestions:
Reduce the water in the mix design; use only as much as needed for a good workable consistency. Another option is to allow longer drying time in between coats; do not apply the next coat even if the previous coat "looks" firm.

Wind Velocity: Wind velocity or air movement, especially under highly humid conditions, helps sealer dry faster than without any air movement. A light breeze assists in the dissipation of water and volatiles from the immediate vicinity.

On the other hand, sealer may dry too fast for properly handling windrows, under breezy conditions at low humidity (20% to 25%).

Mix design alteration suggestion:
Consider adding a bit more water if the sealer is drying too fast for proper flow and leveling of the wet sealer.

It's important contractors follow the mix design guidelines as suggested by their sealer manufacturer then consult with the manufacturer for special situations where the mix designs are not workable. The sealer manufacturer can provide alternatives including material preparation and application to match pavement or weather conditions.

More Mix Design Tips

  • Within the mix design range recommended by the manufacturer, use only as much water as is needed for proper flow and workability. Excessive water reduces the cured film thickness and may result in premature wear.
  • The amount of sand/aggregate may be adjusted according to the pavement usage. A smaller amount of sand might be acceptable for low-traffic pavement with a tight profile while a higher sand loading may be essential for rough pavement, medium traffic, or inclined surfaces.
  • The sand/aggregate loading should not exceed 4 to 5 lbs. per gallon of the concentrated sealer because, being filler, sand will absorb binder as well as water. By absorbing binder, the sand becomes an integral part of the coating. Above 5 lbs. sand absorbs too much binder to be available for adhesion to the pavement. The coating becomes too rigid to flex with the pavement, and the pavement might show adhesion problems.
  • Mesh size of the sand/aggregate must be within 50 to 60 mesh size range because the finer the sand, the higher the number of particles per pound, and the higher the total surface area and higher binder absorption will be. Sand with 100 mesh size has eight times the number of particles and twice the surface area than 50 mesh sand. The binder and water absorption is directly related to the surface area.
  • Use additives where they add a definite value or solve a situation. Ask your supplier about the specific role of the recommended additive and how it will benefit the overall performance.
  • Ignore suggestions to use vinegar, Elmer's glue, or magnesium chloride, etc. as additives. They may damage your sealer. When in doubt, discuss your plans with your materials supplier.

Girish Dubey is president of STAR Inc., Columbus, OH.